Oogoo & epoxy resin mold casting

Opening the door to casting dimensionally complex parts.

14 replies to this topic

#1 shmmee

shmmee

    Member

  • Members
  • 467 posts

Posted 15 March 2012 - 11:16 PM

Oogoo (silicone caulk + corn starch) mold casting:

This builds upon work done by SgNerf on NH: http://nerfhaven.com...=1
With out his ground breaking work and discoveries this certainly wouldn't be possible.

Yes this mod involves oogoo (silicone caulk thinned with mineral spirits and corn starch). Do not get scared or intimidated by this mod. Start by asking a simple question: “Can I make Mac N' Cheese?” Mac N' cheese has 4 basic steps:
Boil noodles, Drain noodles, Melt and combine ingredients, combine cheese sauce with noodles. Making an Oogoo mold has 4 steps – no heat required! Mix oogoo, coat part in oogoo, place coated part in tub full of oogoo and once cured slice part out of oogoo! Wow you have a mold! If you posses the mental and physical capacity to make Mac N' cheese over a stove top, you should be able to do this too. It just stinks a little more than Mac N' cheese...

Changes from the SgNerf method: A cheaper and widely available mold medium is used. The part is entirely coated in the mold medium, and placed in a small tub – slightly larger than the part. The part is then sliced out and the mold separated. The result is that the entire part is duplicated – not just one side – opening the door to casting dimensionally complex parts – like a lanard hand cannon catch:
Posted Image

Here's what will be needed:

Posted Image
Silicone caulk (not ge II) the super cheap opaque $3 tube with black lettering from walmart works beautifully!
Corn starch (baking aisle at your local grocery store)
Silicone spray lubracant (mold release agent)
Mold containers (plastic baby food tubs work very well for small parts) large enough for the piece being duplicated to lay flat in (you'll be nearly filling it with oogoo, so a huge tub for a small part will waste a lot of material)
Posted Image
Gallon sized plastic bags (optional)
stirring sticks (popsicle sticks are suggested)
Sharp knife (to slice the mold around the part)
Devcon plastic steel two part epoxy (acehardwareoutlet via amazon.com gave me the best deal on shipping. I got (3) 2 oz sets for about $12 shipped.
Mold dead space filler (air soft pellets, washers, pennys... anything that you can fill the top of your tub to press the mold halves together while your epoxy cures.)

Yeah, you might be able to use RTV silicone, but seriously it's probably a lot thicker and is certainly more expensive... $10 spent on a tube of caulk and a pint of mineral spirits from walmart (liberate the corn starch from your mom's pantry) would give you enough material for at least 6 baby food tub molds with enough mineral spirits left over for another dozen molds.

Parts to cast...
I've selected breakage and wear prone parts: BBBB trigger, marshmallow xbow catch, and a lanard hand cannon catch. The bbbb trigger and xbow catch are pretty simple, and could of worked with SgNerfs original method, but the hand cannon catch is pretty complex and wouldn't of worked.

Make sure you have your parts before you start mixing oogoo.

The process:

Mix oogoo...
You can either mix it in a plastic bag, or stir everything together in the mold container. The plastic bag will contain the stench of the silicone, but the container is a little easier to mix in and it will be easier to avoid making too much oogoo. Begin by squeezing out enough caulk to fill enough of your mold to cover your part. You can either use the plastic bag, or the mold container. I actually found it easier to mix in the mold container, but I had a pretty severe cold that day and couldn't smell a thing. Shake your mineral spirits up a bit (make sure the cap is secure) and pour in about half as much mineral spirits as you have caulk and mix the two together. The mineral spirits will thin out your caulk so it can penetrate smaller crevices release air bubbles and produce a higher quality cast. You want the consistency to be a little thicker than honey. Add more mineral spirits as needed.

Once mixed add a slightly rounded table spoon (small baby food tub sized mold) or two (for a bigger mold) of corn starch and mix that in too. Corn starch speeds the cure time from weeks to over night. If you've mixed in a plastic bag, cut the tip off the bag and squeeze the contents into your mold container.
Mixing in the tub:
Posted Image
Mixing in the bag:
Posted Image

Molding the part:
Spray your part with silicone (don't hose it, just give it enough to make it shiny), and shake it off. Coat it in oogoo, try to get oogoo in all the small crevices, and bury it in your mold container. Try to bury it so it's resting level, and either near the top or bottom of the mold. You'll need to have a pretty good idea of where it is when you go to chop it out. You can have a second part in the mold so long as they aren't touching. I cast the BBBB trigger in the bottom of a tub, and marshmallow x bow trigger at the top. Might as well make your mold multi-task.
Part coated:
Posted Image
Part in tub:
Posted Image
Hello little marshmallow xbow catch!

Put the lid on and let it cure for at least 12 hours or until firm and solid. Remove it from the mold, and set it aside to de-stink for another 3-4 days.

Posted Image

When I pulled the marshmallow xbow catch from it's tub I noticed an air pocket exposing the part. I mixed a little more oogoo, patched up the pocket and put it back in the tub. Long story short, you can repair your mold as needed.

Once you can handle your mold, grab a sharp knife, poke and squeeze the mold until you have a good idea of the parts location, and plan your cut. You want to make ONE cut all the way around the part so that you can pull the two halves apart like a clam shell. Carefully slice until the halves separate and the part is free. Yea! This should be a slow surgical process. You have a negative of the part trapped in the mold! If there are any large air bubbles open in the mold, patch with oogoo, replace the part and let it cure again.
Posted Image

Lets cast a part:

Spray a rag with silicone spray and wipe down your mold.

Mix enough plastic steel to fill the mold. Wow that stuff is thick! (you can always mix more if needed, the cure time is reasonably forgiving) and smear the plastic steel into the bottom half of the mold. Fill it till it's level, and place it in the mold container. Next fill the top half of the mold and place the top half on the bottom half inside your mold. Make sure you orientate both halves correctly! You need to apply even pressure from the top of the mold. I'm still figuring this part out, and right now I'm thinking the best way is to fill the dead space with something like airsoft pellets and put the lid on. Lacking air soft pellets, I used pennys. Washers may also work, but I think airsoft pellets would work best – being both small and spherical. Sorry I don't have a picture of that. Just imagine a tub partially filled with cured oogoo, with the rest of the tub filled to the brim with what ever small randomness you can come up with. Placing the lid on the tub compresses the randomness which presses the mold halves together while the epoxy cures.

Let the part cure overnight, (or at least 6 hours) remove it and inspect for defects. If there are any bubbles, mix more liquid plastic, fill the gaps, and return the part to the mold. Once fully cured (24 hours), remove, reinspect and trim any excess. Drill any mechanical holes needed, and install. I'm shipping the hand cannon catch off to TaerKitty for testing and evaluation. I don't use my hand cannon much, might as well have have it put through the wringer by someone who does. So don't ask me how durable the end product is yet. I don't know. I expect that they'll wear much better than the standard stock ABS plastic parts, but that is yet to be proven. Right now it's only proven that they can be made.

Posted Image

I'm also very interested in seeing what anyone else has cast. I would consider it on topic so, feel free to post pictures of your work here also.

Edited by shmmee, 15 March 2012 - 11:20 PM.

  • 0
"and we should respect the people who make our blasters. Even if we do molest the hell out of them..."
~BritNerfMogul


#2 Eik

Eik

    Member

  • Members
  • 120 posts

Posted 16 March 2012 - 12:34 AM

This is excellent - I tried doing something like this months ago, but didn't add enough cornstarch so it took forever to cure.
  • 0

#3 Draconis

Draconis

    I am not Lord Draconical

  • Members
  • 2,712 posts

Posted 16 March 2012 - 01:18 AM

Nice to see this moving forward. I am curious to see how well the parts hold up to modified blaster abuse. Another possibility may be to use fiberglass resin with filler material.
  • 0
[15:51] <+Noodle> titties
[15:51] <+Rhadamanthys> titties
[15:51] <+jakejagan> titties
[15:51] <+Lucian> boobs
[15:51] <+Gears> titties
[15:51] <@Draconis> Titties.
[15:52] <+Noodle> why is this so hard?

#4 blitz

blitz

    Member

  • Members
  • 285 posts

Posted 16 March 2012 - 05:44 AM

I think I love you. Awesome project, can't wait to see how this turns out.
  • 0
Blitz, member of the FNBS
"sexual innuendo no intendo"

#5 arfink

arfink

    Member

  • Members
  • 246 posts

Posted 16 March 2012 - 11:28 AM

I might make a slight suggestion here. To remove the step of cutting of the mold later, it might be advisable to mold in this fasion:
First, dip/coat the part as needed. Then put the part down in enough oogoo to cover half of it. Insert some small blocks of wood to use for registration. The part and blocks of wood should be sticking halfway out of the oogoo. Cure, then use more oogoo to make the other side. See here for more details of how you'd do that, only with chocolate:

http://offbeatbride....olate-dice-mold

But personally I'd avoid all that fuss and cut the mold instead, preferably by doing a two-step pour, where the top layer has some dye in it. You'd still get the benefit of curing the whole batch at once, with an obvious color gradation to follow so as to know where to cut.
  • 0
A2GS + 4 meg RAM + 128 meg CF + 9600 Baud Lantronix = WIN

#6 hamoidar

hamoidar

    Member

  • Members
  • 367 posts

Posted 16 March 2012 - 08:12 PM

I wonder if it would be possible to replicate larger objects/crossbow shells. Sure, it would take a huge amount of oogoo and casting material, but it would quickly pay for itself. After all, once you made one mold, you could use it many times.
  • 0
NerfHaven > Your control panel > Profile > Change Signature > Inserts dumb sig > What! No pictures! > Inserts next best thing: http://nerfhaven.com...howuser=114052' class='bbc_url' title='External link' rel='nofollow external'>Best thing on Nerfhaven!

#7 shardbearer

shardbearer

    Member

  • Members
  • 177 posts

Posted 16 March 2012 - 08:57 PM

I love all the things we (really just shmee) are using Oogoo for. Great work.

@Hoidar Keeping the Oogoo from sagging in the middle would be very hard, and you would get much thinner or even nonexistent parts of the shell in the center. Some kind of hard mold material would work, and if it's a putty, you don't need to have the container and could use much less material. Cutting it open though...maybe make the two sides separately?

And really, what's with this community's obsession over crossbow shells?
  • 0

#8 shmmee

shmmee

    Member

  • Members
  • 467 posts

Posted 17 March 2012 - 09:02 AM

I might make a slight suggestion here. To remove the step of cutting of the mold later, it might be advisable to mold in this fasion:
First, dip/coat the part as needed. Then put the part down in enough oogoo to cover half of it. Insert some small blocks of wood to use for registration. The part and blocks of wood should be sticking halfway out of the oogoo. Cure, then use more oogoo to make the other side. See here for more details of how you'd do that, only with chocolate:

http://offbeatbride....olate-dice-mold

But personally I'd avoid all that fuss and cut the mold instead, preferably by doing a two-step pour, where the top layer has some dye in it. You'd still get the benefit of curing the whole batch at once, with an obvious color gradation to follow so as to know where to cut.


Taerkitty suggested this on Nrev. It should make things much simpler. He also suggested putting on a coat of vasoline to any surfaces that we don't want to be bonded. That should really help avoiding the difficult slice.

The problem with oogoo casting very large objects like cross bow shells - is that there is some shrinkage as the oogoo off gasses. More so with the addition of mineral spirits (just some bob predicted this back when I first started working with oogoo). With small parts it's not too noticeable. At the scale of a crossbow shell, it would probably be a deal killer.

At this scale - for the sake of cost and repeatability - any one interested in casting very large pieces should really consider looking into "sand casting". It's an old forging process still used today. Sand is mixed with oil till it sticks like playdough. A part is buried in a half frame and sand packed around it. A top half of the mold is placed over it, and more sand is packed in. The two clam shell halves are separated, the part is removed, and a pour port is installed. The cavity is then normally filled with molten metal, but we might be able to do the same with epoxy.

It is also worth noting that pointman9 has demonstrated on another forum that castings can also work using normal epoxy as the casting material (he was using SgNerfs method) for non stressed parts like barrel spacers can work beautifully. It doesn't have to be devcon liquid metal.
  • 0
"and we should respect the people who make our blasters. Even if we do molest the hell out of them..."
~BritNerfMogul


#9 hamoidar

hamoidar

    Member

  • Members
  • 367 posts

Posted 17 March 2012 - 03:35 PM

I love all the things we (really just shmee) are using Oogoo for. Great work.

@Hoidar Keeping the Oogoo from sagging in the middle would be very hard, and you would get much thinner or even nonexistent parts of the shell in the center. Some kind of hard mold material would work, and if it's a putty, you don't need to have the container and could use much less material. Cutting it open though...maybe make the two sides separately?

And really, what's with this community's obsession over crossbow shells?

Why would the oogoo sag in the middle? If you are making the mold in a large bin, on a table or floor, how could it sag? It's not like you would cast it in the same paper-thin plastic detailed here.
  • 0
NerfHaven > Your control panel > Profile > Change Signature > Inserts dumb sig > What! No pictures! > Inserts next best thing: http://nerfhaven.com...howuser=114052' class='bbc_url' title='External link' rel='nofollow external'>Best thing on Nerfhaven!

#10 shmmee

shmmee

    Member

  • Members
  • 467 posts

Posted 19 March 2012 - 08:22 AM

It doesn't sag - it shrinks. The bigger the mold - the more pronounced the shrinkage will be. Even the bbbb trigger mold (as small as it is) has shrunk enough that it doesn't touch all 4 walls at the same time. It challenges the alignment of the mold halves when the mold becomes smaller than the container. A mold the size of a blaster shell would have serious issues. Like I sais earlier - at that scale we should look at adapting an old forging process called sand casting.
  • 0
"and we should respect the people who make our blasters. Even if we do molest the hell out of them..."
~BritNerfMogul


#11 Paloose

Paloose

    Member

  • Members
  • 143 posts

Posted 19 March 2012 - 12:29 PM

Sand casting is a casting process, not a forging process.
  • 0

#12 Zorns Lemma

Zorns Lemma

    Sir Scrt

  • Moderators
  • 1,277 posts

Posted 19 March 2012 - 03:55 PM

Plastic epoxy or urethane resin is probably better for casting than things similar to JB Weld. You're not looking for total bond strength but rather tensile/yield/elasticity and impact resistance.

High strength epoxy on the other hand ends up being rather brittle.
  • 0
"In short, the same knowledge that underlies the ability to produce correct judgement is also the knowledge that underlies the ability to recognize correct judgement. To lack the former is to be deficient in the latter."
Kruger and Dunning (1999)

#13 mak

mak

    Member

  • Members
  • 32 posts

Posted 19 March 2012 - 05:51 PM

Plastic epoxy or urethane resin is probably better for casting than things similar to JB Weld. You're not looking for total bond strength but rather tensile/yield/elasticity and impact resistance.

High strength epoxy on the other hand ends up being rather brittle.



First off if this sounds n00bish of me, but can you mix them together and get something in the middle?
  • 0
Pm me if if you hove a supermaxx1000 for sale.

#14 shmmee

shmmee

    Member

  • Members
  • 467 posts

Posted 19 March 2012 - 06:13 PM

Plastic epoxy or urethane resin is probably better for casting than things similar to JB Weld. You're not looking for total bond strength but rather tensile/yield/elasticity and impact resistance.

High strength epoxy on the other hand ends up being rather brittle.


Well, I'm thinking you are probably right. I was cleaning the hand cannon catch by clipping off a goober that was hanging out in the elbow, and when I made the cut the entire arm came off and the goober stayed put. I epoxied it back together and threw it back in the mold thinking it wasn't fully cured - even though a full 24 hours had passed. I haven't been able to get back to it yet, but plastic steel might be too brittle to cast parts from.
  • 0
"and we should respect the people who make our blasters. Even if we do molest the hell out of them..."
~BritNerfMogul


#15 Pointman9

Pointman9

    Member

  • Members
  • 131 posts

Posted 19 March 2012 - 09:27 PM

Well, I'm thinking you are probably right. I was cleaning the hand cannon catch by clipping off a goober that was hanging out in the elbow, and when I made the cut the entire arm came off and the goober stayed put. I epoxied it back together and threw it back in the mold thinking it wasn't fully cured - even though a full 24 hours had passed. I haven't been able to get back to it yet, but plastic steel might be too brittle to cast parts from.

The things that I have made (barrel spacers and such) are actually not from epoxy, but from casting resin. If you search on Amazon for "Casting resin" you should be able to find it. It takes up to three days to cure but is remarkably strong, but not brittle. On a side note, I made a mold for tacti-cool rails and my first casting should be done in a couple of days.
Posted Image
  • 0
There is no such thing as overkill. There is only cost efficiency.